Arc Metal Powder Printer

In this project I want to build a metal powder printer that uses an arc instead of a laser.

Public Chat
Similar projects worth following
In this project I want to build an open source metal powder printer that uses an arc instead of a laser, because an metal melting arc can be created with simple electronics that are much more affordable and also safer to handle than a high power laser.

My first goal was to test whether it works at all, what I just could confirm recently: It's possible to create low quality single layer objects at the moment.
My next goal is to increase the quality or reduce the heated area spot and also find a software concept for the operation of the machine.
The machine could operate in the same way as my DIY Inkjet project (Drop on Demand or in this case Arc on Demand) and so it could be possible to use the same software for both machines. The development could also lead to the same 3D powder bed printer design for both machines in which the DIY Inkjet could be developed to a binder jet printer.

  • DC Side Switching

    Dominik Meffert3 days ago 0 comments

    I've built another MOSFET board for switching of the DC side to make very fast switching of the power source possible.

    I tested it out and realized that the too long ON-times which I thought were caused by the rectifiers capacitor were still there and therefore were caused by the GCODE.

    So better GCODE is needed.

    I ordered some fittings, which I want to use for building a watercooled electrode mounting bracket. They should arrive by the middle of the next week. 

  • Testing everything together

    Dominik Meffert10/18/2020 at 03:13 0 comments

    Now that the arc starter, arc power, stepper driver and printer controller work it is time to test everything together.

    In this test I tried continuous mode for melting the powder. The result looked good but was only partially melted solid. By trying out a lower moving speed the result got not really better but the tungten electrode melted due to the heat and no cooling. The 3D printed mounting bracket also melted, what was ok, because it was not designed to withstand high temperatures. I think I will design a watercooled all-metal toolhead in the future which can handle the temperature and prevent the electrode from melting.

    I did another test and this time I tried to print a dot matrix with the idea that multiple dots  placed close to each other can create a solid structure, which was the case.

    I think with this method the amount of heat/energy can be controlled more precisely than with continuous mode:

    I could be wrong, but I think with continuous mode there would be only the power (Amps/Voltage Setting) and the moving speed adjustable and with dot matrix mode there would be also the exposure time and space between dots adjustable, what I think could lead to a more precise and reproducable heating. I think it would also be possible to add short cooling time between the dots to prevent the heat from the pulses from adding up on each other what could prevent overheating of the electrode and spreading of the heat in the powder. Maybe doing so could also reduce the width of the printed lines, what would lead to more pecision.

    First printed single layer object - there is plenty room for improvements :)

    I think a thing that has gone wrong in this test was that the switching of the welding power has been slower than the actual setting. The cause for that is, that I'm currently switching the AC side with a SSR before the rectifier and its capacitor which has to charge and discharge, what I think is slowing down the switching time.

    I did that because the SSR was the only semiconductor part which not got destroyed from the arc starter.

    I replaced the continuous arc starter with a single pulse arc starter a while back and did not try another MOSFET out. Maybe it would work with the new arc starter and I will test it out in the next few days.

    Fried MOSFETS were a huge problem in the construction of this project.

    The first time I got the new arc starter to work the MOSFET got fried after some time, I assume from ESD on the gate.

    I designed a new pcb with four 7.5V zener diodes between gate and source to clamp the voltage to 15V and two 265V TVS diodes between drain and source to clamp the voltage to 265V. The MOSFET is a IRFP460 driven with 12V.

    This MOSFET board switches the arc starter and maybe such a board would also work for the arc power.

    I hope this design will last long, because I have no idea what else I could do to prevent the MOSFET from dieing.

  • 6 Channel Optical Controller

    Dominik Meffert10/18/2020 at 00:03 0 comments

    To get the machine operational I needed at least 6 optical channels for controlling it from a for the controller and the notebook noise-safe distance. Step and Dir channels for two stepper drivers and signals to turn on the arc starter and arc power.

    The system works very reliable and with the new single pulse arc starter the motors are no longer noticable affected by the arc starter, even though my TV turns still on and my notebooks screen output crashes when it is too close to the arc. The optical cable is a cheap 25m toslink one that I cut in six 4m pieces to have enough room between the notebook and the printer (about 2m). The controller which is an Arduino Mega + Ramps 6 plus is connected to the lasers which are hotglued in 3D printed brackets which also hold the fiber cables. At the other end are also 3D printed brackets with no-name "ISO203" unmodulated laser receiver modules. I soldered the parts from the module (sensor, capacitor, resistor) to a pcb to prevent the sensor from false readings which it has sometimes due to vibrations when placed in the original mounting slot.

  • Pulse Welding

    Dominik Meffert10/07/2020 at 00:14 0 comments

    I always wanted to operate the machine in pulsed mode, to focus the heat on a small spot without spreading it to much in the powder, but I did not know how to do it until I recently figured it out. I saw a video by Electroboom ( in which he builds a taser from a car ignition coil and this circuit was exactly what I needed for a new arc power source. For controlling the pulses I'm using a MOSFET connected to a optical receiver controlled by a microcontroller instead of the continuous HF starter that I used before. By doing so it was also possible to simplify the design and to reduce the noise a bit.

    I tried out another transformer with a higher output voltage, because with 60VAC output/86VDC rectified I could not get a stable arc which would be needed for testing out longer exposure times.

    I tried out more current and at this setting it seems to be enough for melting the powder - even with a very short pulse (not shown in the video). It maybe could also be used for engraving metal in pulsed mode to prevent heat deformation. So I think the next thing could be getting the stepper motors and printer controller to work for testing out melting pattern into the powder and drawing/engraving something on metal. If the current setting will turn out to be still to less powerful I could double power from 600W to 1200W with a more powerful transformer + power resistor combination. I also looked into using an inverter based power source, but I think that will make the machine to complicated to rebuild and so I will likely stay with the current transformer + resistor design. I think if adjustable current settings would be needed, I could add some power resistors for defining the upper current limit and add switchable resistors for further reducing the current if needed. But maybe changing the pulse time would be enough for heat regulation.

  • All-Optical Control

    Dominik Meffert09/27/2020 at 22:44 0 comments

    Now, that the welding system can operate relatively stable it's time for the printer controller and because the machine creates strong electromagnetic interferences, which can turn my TV on and crash its display, the display of my notebook running on battery and every printer controller that I connected to it, I decided to control the machine from a separate completely electrically isolated unit via fiber optic (toslink) cables.

    Maybe there could be a way to get a printer controller running in the same machine frame with shielding + filtering, but I think that would be much more complicated and time consuming than just placing the printer controller some distance away from the machine. I also think transmitting endstop, stepper and trigger signals via laser is an interesting approach.

    Like you can see/or hear in the video the stepper driver or even the motor get affected by the noise and "stalls" a bit, which could be something that needs to be fixed. Maybe shielded motor cables, DC line filtering, ferrite cores on the cables or/and a grounded enclosure for the stepper drivers could help. I'm very glad that the stepper drivers are less noise sensible than the printer controller which crashes as soon as the HF starter turns on, when placed in the machine.

    I ordered one more stepper driver for 2D pattern powder sintering tests.

  • A few Design Changes

    Dominik Meffert09/24/2020 at 13:18 0 comments

    In the last few days I tried to improve the circuit to get it ready for long operation times.

    Things that I changed are:

    - Replaced the transformer to get 60VAC 500VA, rectified around 86VDC open circuit and around 78VDC with the load.

    - Removed the watercooler and added 12pieces 4 ohm 100W resistors to get 12ohm resistance.

    - Added a line filter.

    - Placed the HV supply on a pcb.

    - Replaced the tesla circuit's ceramic capacitor with WIMA FKP1 capacitors.

    - Added a capacitor across the coupling coil for filtering.

    - Replaced the lightbulp with 4pieces 100ohm 100W capacitors to get 100ohm of resistance to discharge the welding capacitor and prevent random firing of the arc, because of the HF arc charging the rectifier capacitor. (Maybe at some point I will find a better solution, but for now it's ok.)

    - Got a SSR to work by adding a snubber circuit (1nF 20kV capacitor + 20ohm resistor) to its output and zener diods to its input + switching it with 12V.

    The next thing will be changing the optical trigger so that the HF arc and welding arc can be controlled separately.

  • Protecting the Welding Circuit from HV + Workaround

    Dominik Meffert09/10/2020 at 13:51 0 comments

    While testing today, I figured out that the HF Start loaded the rectifier capacitor, even when I put a MOV or capacitor in parallel. That caused a decrease in arc strenght and after loading the capacitor to a certain voltage an high power discharge on the tungsten electrode.

    I tested it again with nothing but the HF Start coupling coil connected to the rectifier and its capacitor still gets loaded, so it is definitely caused by the HF Starter.

    By connecting a capacitor in parallel together with the 400ohm resistor in series to the rectifier + reducing the electrode to workpiece distance, I could reduce the loading of the rectifier capacitor to a minimum. Thanks to @Bharbour for the great advice.

    The next problem was that as soon as there was a voltage from the welding source on the welding lines (open circuit), what also included a charged rectifier capacitor, the HF Starter arc did no longer work for some reason.

    But at the end I was able to get it to work with a simple workaround - Maybe no permanent solution, but for now it's good because it works.

    I added a 15W lightbulp as load to the rectifier to discharge its capacitor as soon as there is no longer power from the welding source, what starts the HF arc again. The lightbulp also indicates that there is power from the welding source on the lines what is also a good thing, so maybe I will keep it.

    I think there will be a lot to do in terms of emi/rfi protection, what could end up to be really complicated. I will try many things out and hope that I can find a solution for it over the time.

  • Destructive testing and Continuous HF Start

    Dominik Meffert09/08/2020 at 14:32 4 comments

    I spent the weekend testing stuff to destruction - not intended but I figured some things out.

    - I tested a DC SSR which either never worked or failed at the very beginning.

    - An AC SSR before the rectifier seems to work for now.

    - The four 100W 100ohm resistors seem to get too hot (even with the active cooling) for continuous operation, so I maybe will try something different for current limiting, like an inverter circuit or a saturable reactor.

    But the part I want to get right first is the HF Start Circuit.

    Initially I had planed to pulse the HF Start and Work Current together to keep the temperature on the powder not higher than needed and to put less stress on the electronics.

    But while testing this I figured out that the arc ignited not every time and the HF HV ignition arc got weaker over time until at some point the HF Starter stopped working completely.

    After that I spent some time building an arc detecting circuit which could detect whether the arc has ignited and turn on the HF Start if it would extinguish. (Which I will likely never use).

    I stopped working for a day because I had the false assumption that the Flyback transformer was the part that had failed and I ordered a new one and some parts to build a different flyback driver, until I tried building a new simple single mosfet driver (IRFZ44N + 470ohm resistor on the gate + 6+6 turns flyback/primary coil) for testing the transformer and... the transformer still worked. So the driver must have failed which I think was caused by turnung it on and off at a high frequency. I tested the same driver (6 IRFZ44N in parallel) with the transformer for half an hour and it did not fail, so I think the problem was not caused by mosfet overheating, but by the high frequency on and off switching.

    With the driver I built yesterday I tested out the HF Starter again and the HF HV iginition arc got still weaker over time until even the spark gap stopped working. I disconnected the transformer from the circuit and it still worked and so it could only be the capacitor which must have had failed and this was the case. After replacing the capacitor with a new one it worked again, but after a short time the arc got weaker again until the capacitor failed again.

    I think what happened was the capacitor (a 20kV 1nF Ceramic one) failed over time due to the high frequency of loading and unloading through the spark gap.

    So I ordered 10 pieces WIMA FKP1 15nF 1600V DC capacitors which I'm planning to connect in series to increase the rating to 16000V DC 1.5nF. I read in a tesla coil forum that they are better for the high frequency and I hope they will not fail like the ceramic ones.

    I think if I can get the hf hv ignition arc to work continuously I can just pulse the work current whit the SSR and everything (maybe) will be fine. Until the next problem appears :)

    I figured out the reason for the death of many ceramic capacitor beside that they are not suited for HF. It was the spark gap. For some dumb reason I set it 3 times as wide as planned what leaded to the premature dead of the capacitor after under 2 minutes.

    I set it to 2mm what I think should give me around 6000V and with a fresh capacitor it is enough for a 5mm spark at the tungsten electrode. I will test out how long the ceramic capacitor will last until it gets destoyed (they are not expensive).

    The capacitor (still the ceramic one) lasted over an hour and would likely continue working for a long time without failing completely, but it was clearly visible on the arc that it was no longer working at "full power". I think/hope the WIMA capacitor will perform even better, but an hour is not bad and enough for testing some things out.

    After letting it run for about 1.5 hours the spark gap was covered in an unknown (by me) yellow dust.... maybe it could be vaporised metal from the screws.

    Does anyone know what that dust is?

    After turning the machine off for a moment and on again, the...

    Read more »

  • How it started + Test Stand

    Dominik Meffert08/22/2020 at 14:39 0 comments

    In this project I want to try melting metal powder with an arc in an inert gas chamber to create 3D objects. Inspired by HomoFasciens video in which he burned holes into a piece of paper to print with an hacked arc lighter, I started this project.

    First I connected an arc lighter module to a 3D printer and printed on steel powder which changed its color and bond toghether a bit. 

    After a short time the arc lighter module stopped working, so that I thought about building a more capable power source. 

    So I spent some time of research, to learn how to build a HF starter to start the arc without touching the powder and built one.

    I tried different voltages, currents, AC and DC and figured out, that it worked the best with rectified mains voltage which is for safety isolated from ground via a 1:1.09 transformer and gives 340V DC. I added 4x 100ohm 100W power resistors to limit the current to 0.85A, what seems to be enough for melting the powder.

    With 340V DC the arc ignited every time and kept on going on the last try until I shut it off. I tested it on a distance >1mm.

    I tried to test the welding system on the printer, but it creates so much emi/rfi noise that the printer controller keeps rebooting as long as it is active.

    So I'm currently working on a way to shield the printer controller from noise. For doing so I'm planning to send the trigger signal for the arc via an optical toslink cable, I'm also planning to use shielded cables for the stepper motors, place the controller in a grounded metall box and use Trinamic's StallGuard feature for homing without limit switches. Hopefully that will make printing with an HF start welder possible.

    I'm currently working on a test stand for printer designs, which will contain the welding system and printer controller.

    It will be a bit like a shelf on which the printer (mechanics + motors) will be placed.

    The printer will later be covered with a transparent enclosure which will then purged with shielding gas.

    Maybe the dimensions of 1000*600mm are a bit too large, but I don't know the dimensions of the later printer so I built the test stand a bit larger.

    I will try to find a good place for all parts and complete the test stand in the next days.

    I wired the welding circuit, what's left is the trigger circuit and the printer controller.

    Only the printer controller left...

View all 9 project logs

Enjoy this project?



dekutree64 wrote 10/18/2020 at 01:41 point

Interesting idea. Sort of like electric discharge machining in reverse :)

  Are you sure? yes | no

Bharbour wrote 09/08/2020 at 16:16 point

There might be some useful ideas in this project:

All the newer solid state (vs solid iron :) ) welders that I have looked at, control current by PWM on the DC output. They have enough inductance on the output of the circuit to keep the current rise rate within the bandwidth of the PWM and control hardware. I have done very small current sources (2 - 3A) with this approach and it works well. This approach keeps the power dissipation down to a reasonable level.

  Are you sure? yes | no

Dominik Meffert wrote 09/08/2020 at 17:34 point

Thank you very much for the link, I will check it out :)

  Are you sure? yes | no

Dan Maloney wrote 08/24/2020 at 20:38 point

I really like this idea, assuming that I understand it - you're basically sintering the powdered metal with the arc in a controlled fashion, right?

Have you thought ahead to how the Z-axis dimension will work? Seems like you'll either have to add more powder to the top or sink the growing print into the powder bed as you build up the print.

  Are you sure? yes | no

Dominik Meffert wrote 08/25/2020 at 08:27 point

Hi Dan,

Yes you are right. I want to try sintering the steel powder with an arc in a shielding gas chamber. For the Z axis I'm planning to build a printer with two pistons and a recoater like on a SLS printer, but first I want to test it with a single layer to figure out whether it is possible at all.

  Are you sure? yes | no

Dan Maloney wrote 08/25/2020 at 16:42 point

Good stuff, following with interest. I like this approach much better than the "CNC-MIG welder" ideas I've seen so many times. Seems more elegant.

  Are you sure? yes | no

Similar Projects

Does this project spark your interest?

Become a member to follow this project and never miss any updates